| Parameters | Value | Requirement of SNI 0302:2014 |
| Chemical Properties |
|
|
| Insoluble residue | 13.11 ± 0.06 | NA |
| Silicone dioxide, SiO2 | 23.84 ± 0.21 | NA |
| Ferric oxide, Fe2O3 | 3.24 ± 0.09 | NA |
| Aluminum oxide, Al2O3 | 8.08 ± 0.25 | NA |
| Calcium Oxide, CaO | 57.52 ± 0.16 | NA |
| Magnesium oxide, MgO | 0.82 ± 0.05 | Max 6.0 |
| Sulfur oxide, SO3 | 1.63 ± 0.07 | Max 4.0 |
| Loss of ignition | 4.52 ± 0.05 | Max 5.0 |
| Alkalinity as Na2O | 0.50 ± 0.04 | NA |
| Free lime | 0.94 ± 0.09 | NA |
| Physical Properties |
|
|
| Fineness, by Blaine Apparatus, m2/kg | 317 | Min 280 |
| Setting time, Vicat test - Initial. minute - Final, minute |
191 270 |
Min 45 Max 240 |
| Autoclave expansion - Shrinkage, % - Expansion, % |
NA 0.12 |
Max 0.8 Max 0.2 |
| Compressive strength - 3 days, kg/m2 - 7 days, kg/m2 - 28 days, kg/m2 |
184 234 317 |
Min 130 Min 200 Min 280 |
| Air content of mortar, % (v/v) | 5.9 | Max 12 |
| Density, g/ml | 2.94 | NA |