ASPHALT BINDER TESTS | |||||||||||
SAMPLE ID: | IZMIT B50/70+ 0.3% ZYCOTHERM |
| |||||||||
TEST METHOD |
| TEST RESULTS | SPECIFICATION | ||||||||
(RTFOT) ROLLING THIN FILM AGED ASPHALT BINDER, TS EN 12607-1 | |||||||||||
MASS CHANGE % | 0.13 | ≤1.00% | |||||||||
(DSR) DYNAMIC SHEAR RHEOMETER TS EN 14770, AASHTO T 315 | |||||||||||
TEST TEMPERATURE ’C | G*, kPa | PHASE ANGLEȭ’, | G* sin&, kPa | ≥2.2 kpa | |||||||
64 | 2.573 | 86.41 | 2.5779 | ||||||||
70 | 1.11 | 87.48 | 1.1208 | ||||||||
(PAV) PRESSURE AGING VESSEL AND (RTFOT) AGED ASPHALT BINDER, TS EN 14769, AASHTO R28 | |||||||||||
(DSR) DYNAMIC SHEAR RHEOMETER TS EN 14770, AASHTO T 315 | |||||||||||
TEST TEMPERATURE ’C | G*, kPa | PHASE ANGLEȭ’, | G* sin&, kPa | ≤5000 kpa | |||||||
28 | 5.09 | 54.52 | 4145.3 | ||||||||
25 | 7.95 | 51.15 | 6194.4 | ||||||||
(BBR) BENDING BEAM RHEOMETER TEST, TS EN 14771, ASTM D6648, AASHTO T313 | |||||||||||
TEST TEMPERATURE ’C |
|
|
| ||||||||
−6 | STIFFNESS, MPA | 92.3 | ≤300 MPA | ||||||||
M-VALUE | 0.402 | ≥0.300 | |||||||||
−12 | STIFFNESS, MPA | 193 | ≤300 MPA | ||||||||
M-VALUE | 0.333 | ≥0.300 | |||||||||
−18 | STIFFNESS, MPA | 443 | ≤300 MPA | ||||||||
M-VALUE | 0.264 | ≥0.300 | |||||||||