Sample | Mortar components, g (+standard sand 1350 g) | Slump, mm | Demolding time, days | Compressive strength, MPa | ||||||||
GBFS-1 | GBFS-2 | HCFA-H | HCFA-L | Na2CO3 | NaGlu | LS | Water | 7 days | 28 days | |||
1 | 450 | - | - | - | - | - | 2.25 | 180 | 100 | - | 0 | 0 |
2 | 450 | - | - | - | 4.5 | - | 2.25 | 180 | 121 | >12 | 0 | 15.6 |
3 | 450 | - | - | - | 9.0 | - | 2.25 | 180 | - | 12 | 0 | 20.5 |
4 | 450 | - | - | - | 13.5 | - | 2.25 | 180 | 132 | 5 | 10.9 | 40.5 |
5 | 450 | - | - | - | 13.5 | - | 2.25 | 160 | 107 | 5 | 11.8 | - |
6 | 405 | - | 45 | - | 4.5 | 0.45 | - | 160 | 148 | 2 | 2.5 | 16.0 |
7 | 405 | - | 45 | - | 13.5 | 0.45 | - | 160 | 124 | 1 | 17.1 | 36.2 |
8 | 405 | - | 45 | - | 13.5 | 0.90 | - | 140 | 100 | 1 | 21.2 | 39.0 |
9 | 315 | - | 135 | - | - | 0.45 | - | 160 | 151 | 2 | 1.1 | 4.5 |
10 | 315 | - | 135 | - | 4.5 | 0.45 | - | 160 | 123 | 1 | 4.7 | 18.7 |
11 | 315 | - | 135 | - | 13.5 | 0.90 | - | 180 | 206 | 1 | 21.7 | 33.0 |
12 | 315 | - | 135 | - | 13.5 | 0.90 | - | 140 | 110 | 1 | 31.6 | 43.9a |
13 | 315 | - | 135 | - | 13.5 | 0.90 | - | 160 | 145 | 1 | 21.7 | 32.8 |
14 | - | 450 | - | - | - | - | 2.25 | 180 | 138 | - | 0 | 0 |
15 | - | 450 | - | - | 13.5 | - | 2.25 | 170 | 117 | 5 | 0.8 | 24.9 |
16 | - | 405 | 45 | - | 13.5 | 0.90 | - | 140 | 117 | 3 | 16.1 | 35.1 |
17 | - | 315 | 135 | - | - | - | - | 140 | 122 | 1 | 2.0 | 27.9 |
18 | - | 315 | 135 | - | 13.5 | 0.90 | - | 140 | 115 | 2 | 27.1 | 36.5 |
19 | 315 | - | - | 135 | - | 0.45 | - | 200 | - | 3 | 12.5 | - |
20 | 315 | - | - | 135 | 13.5 | 0.90 | - | 200 | - | 3 | 10.5 | 18.1 |
21 | - | 315 | - | 135 | 4.5 | 0.45 | - | 190 | 114 | 7 | 0.5 | 20.8 |
22 | - | 405 | - | 45 | 9.0 | 0.90 | - | 170 | 133 | 12 | 0.0 | 22.6 |
23 | - | 315 | - | 135 | - | 0.45 | - | 200 | 113 | 5 | 10.8 | 20.9 |
24 | - | 315 | - | 135 | 4.5 | 0.45 | - | 200 | 118 | 5 | 10.8 | 22.9 |
25 | - | 315 | - | 135 | 13.5 | 0.90 | - | 200 | 155 | 4 | 10.8 | 18.9 |
26 | - | 315 | - | 135 | 13.5 | 0.90 | - | 180 | 104 | 2 | 10.4 | 18.8 |