Sampling day | Amount of CIGS TFSP added (%) |
| ||||
Zn | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.72 | 0.48 | 0.32 | 0.26 | 0.20 | −0.953** |
60th | 2.02 | 1.37 | 0.91 | 0.74 | 0.63 | −0.946** |
90th | 2.16 | 1.52 | 1.12 | 0.85 | 0.74 | −0.961** |
120th | 2.87 | 1.94 | 1.25 | 1.00 | 0.76 | −0.957** |
Correlations (r) | 0.950* | 0.952* | 0.942* | 0.940* | 0.884 | - |
Ni | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 2.37 | 1.29 | 1.24 | 0.56 | 0.48 | −0.939** |
60th | 2.38 | 1.39 | 1.32 | 0.58 | 0.65 | −0.930* |
90th | 2.43 | 1.40 | 1.43 | 0.66 | 0.66 | −0.929* |
120th | 2.29 | 1.53 | 1.54 | 0.72 | 0.67 | −0.952** |
Correlations (r) | −0.423 | 0.957* | 0.997** | 0.978* | 0.829 | - |
Al | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.95 | 0.72 | 0.74 | 0.65 | 0.71 | −0.759 |
60th | 1.07 | 0.77 | 1.06 | 1.09 | 1.26 | 0.627 |
90th | 1.15 | 0.99 | 1.42 | 1.16 | 1.33 | 0.499 |
120th | 1.18 | 1.25 | 1.36 | 1.15 | 1.36 | 0.418 |
Correlations (r) | 0.967* | 0.966* | 0.917* | 0.832 | 0.852 | − |
Cr | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.41 | 0.41 | 0.37 | 0.41 | 0.34 | −0.693 |
60th | 0.47 | 0.50 | 0.44 | 0.44 | 0.43 | −0.768 |
90th | 0.47 | 0.52 | 0.48 | 0.48 | 0.47 | −0.305 |
120th | 0.45 | 0.57 | 0.49 | 0.48 | 0.49 | −0.036 |
Correlations (r) | 0.548 | 0.966* | 0.948* | 0.948* | 0.951* | - |
Ga | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.83 | 0.79 | 0.64 | 0.60 | 0.57 | −0.962** |
60th | 0.85 | 0.80 | 0.63 | 0.57 | 0.56 | −0.953** |
90th | 0.86 | 0.82 | 0.63 | 0.61 | 0.57 | −0.945** |
120th | 0.85 | 0.80 | 0.64 | 0.60 | 0.56 | −0.966** |
Correlations (r) | 0.718 | 0.513 | 0.000 | 0.298 | −0.447 | − |
Pb | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.05 | 0.06 | 0.05 | 0.05 | 0.05 | −0.354 |
60th | 0.11 | 0.13 | 0.12 | 0.11 | 0.06 | −0.702 |
90th | 0.12 | 0.13 | 0.11 | 0.11 | 0.11 | −0.707 |
120th | 0.14 | 0.14 | 0.14 | 0.13 | 0.13 | −0.866* |
Correlations (r) | 0.933* | 0.838 | 0.867 | 0.894 | 0.969* | - |
Cu | 0% | 2.5% | 5% | 7.5% | 10% | Correlations (r) |
30th | 0.39 | 0.28 | 0.25 | 0.22 | 0.18 | −0.954** |
60th | 0.63 | 0.49 | 0.48 | 0.45 | 0.34 | −0.945** |