Materials | Sintering density (g/cm3) | Relative density (%T.D.) | Average grain size (µm) | HV10 (GPa) |
MoSi2 | 6.01 | 96.2 | 5 | 8.7 ± 0.3 |
(Mo0.9Cr0.1)Si2 | 6.06 | 99.3 | 14 | 7.7 ± 0.2 |
MoSi2 + 15vol%ZrO2 | 5.84 | 95.0 | 4 | 8.7 ± 0.2 |
(Mo0.9Cr0.1)Si2 + 15vol%ZrO2 | 5.95 | 98.5 | 11 | 7.9 ± 0.2 |