m | Compound | Tc (K) | Ps (μC/cm2) along a axis | Dielectric Constant | Curie-Weiss Constant | ||
ε (r.t.) | ε (Tc) | C (105 K) | Θ (K) | ||||
1 | Bi2WO6 | 973 | - | 200 | 3100 | 1.4 | 1199 |
1 | Bi2MoO6 | 843 | - | 16 | 103 | - | - |
2 | Bi3TiNbO9 | 1213 | - | 100 | - | - |
|
2 | Bi3TiTaO9 | 1146? | - | 140 | - | - |
|
2 | CaBi2Nb2O9 | 923? | - | 80 | - | - |
|
2 | CaBi2Ta2O9 | 873? | - | 140 | - | - |
|
2 | SrBi2Nb2O9 | 713 | - | 190 | 1100 | 0.55 | 663 |
2 | SrBi2Ta2O9 | 608 | 5.8 at r. t. | 180 | 550 | 2.0 | 463 |
2 | BaBi2Nb2O9 | 473 | - | 280 | 540 | - | - |
2 | BaBi2Ta2O9 | 383 | - | 400 | 450 | - | - |
2 | PbBi2Nb2O9 | 823 | - | 170 | 2100 | 1.3 | 783 |
2 | PbBi2Ta2O9 | 703 | - | 180 | 340 | 0.37 | 598 |
3 | Bi4Ti3O12 | 948 | 50//a, 4//c | 140 | 1600 | - | - |
3 | BaBi3Ti2NbO12 | 543 | - | - | - | - | - |
3 | PbBi3Ti2NbO12 | 563 | - | - | - | - | - |
4 | BaBi4Ti4O15 | 693 | - | 150 | 1630 | 2.5 | 608 |
4 | PbBi4Ti4O15* | 843 | - | 220 | 5500 | 1.4 | 825 |
4 | SrBi4Ti4O15* | 803 | - | 190 | 1630 | 0.68 | 758 |
4 | CaBi4Ti4O15* | 1063 | - | 120 | - | - | - |
4 | Bi5Ti3CaO15 | - | - | 150 | - | - | - |
4 | Na0.5Bi4.5Ti4O15 | 908 | - | 200 | 1600 | 0.79 | 883 |
4 | K0.5Bi4.5Ti4O15 | 823 | - | 140 | 1700 | 0.74 | 788 |
5 | Pb2Bi4Ti5O18 | 583 | 0.06 at 508 K | 400 | 5900 | 4.1 | 553 |
5 | Sr2Bi4Ti5O18 | 558 | 3.5 at 528 K | 280 | 1700 | 0.47 | 528 |
5 | Ba2Bi4Ti5O18 | 602 | 2 at r.t. | 360 | - | - | - |
5 | Ca2Bi4Ti5O18 | 726 | - | 40 | 420 | - | - |
5 | Pr2Bi4Ti3Fe2O18 | 1173 | - | - | - | - | - |
5 | Bi6Ti3WO18 | 1023 | - | 100 | 1000 | - | - |