| NO. | W% | HLB | TS% | TIME(min) | rpm | pH | D (nm) |
| 1 | 18 | 5.7 | 2.6 | 40 | 17,000 | 9.8 | 30 |
| 2 | 18 | 5.7 | 2.6 | 30 | 17,000 | 11.2 | 29.2 |
| 3 | 12 | 5.7 | 3.4 | 40 | 17,000 | 9.8 | 21 |
| 4 | 12 | 5.3 | 3.4 | 30 | 13,000 | 9.8 | 27.3 |
| 5 | 12 | 5.7 | 3.4 | 30 | 17,000 | 11.2 | 22 |
| 6 | 18 | 5.3 | 2.6 | 30 | 13,000 | 9.8 | 31.3 |
| 7 | 18 | 5.3 | 3.4 | 30 | 17,000 | 11.2 | 27 |
| 8 | 18 | 5.3 | 2.6 | 40 | 13,000 | 11.2 | 33 |
| 9 | 12 | 5.3 | 2.6 | 40 | 17,000 | 9.8 | 25 |
| 10 | 12 | 5.3 | 2.6 | 30 | 17,000 | 11.2 | 24.3 |
| 11 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 27 |
| 12 | 12 | 5.7 | 2.6 | 40 | 13,000 | 11.2 | 29 |
| 13 | 18 | 5.7 | 3.4 | 30 | 13,000 | 9.8 | 29 |
| 14 | 18 | 5.3 | 3.4 | 40 | 17,000 | 9.8 | 26.5 |
| 15 | 18 | 5.7 | 3.4 | 40 | 13,000 | 11.2 | 27 |
| 16 | 12 | 5.7 | 2.6 | 30 | 13,000 | 9.8 | 26.1 |
| 17 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 27.5 |
| 18 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 27 |
| 19 | 12 | 5.3 | 3.4 | 40 | 13,000 | 11.2 | 24.2 |
| 20 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 28 |
| 21 | 12 | 5.3 | 2.6 | 40 | 13,000 | 9.8 | 24.1 |
| 22 | 18 | 5.3 | 3.4 | 30 | 13,000 | 11.2 | 32 |
| 23 | 18 | 5.7 | 3.4 | 30 | 17,000 | 9.8 | 27.3 |
| 24 | 12 | 5.3 | 2.6 | 30 | 13,000 | 11.2 | 30 |
| 25 | 12 | 5.7 | 3.4 | 30 | 13,000 | 11.2 | 27 |
| 26 | 18 | 5.7 | 3.4 | 40 | 17,000 | 11.2 | 22.3 |
| 27 | 12 | 5.3 | 3.4 | 30 | 17,000 | 9.8 | 25 |
| 28 | 12 | 5.7 | 3.4 | 40 | 13,000 | 9.8 | 23.5 |
| 29 | 18 | 5.7 | 2.6 | 30 | 13,000 | 11.2 | 32.3 |
| 30 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 28 |
| 31 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 27.9 |
| 32 | 12 | 5.7 | 2.6 | 30 | 17,000 | 9.8 | 26 |
| 33 | 18 | 5.3 | 2.6 | 30 | 17,000 | 9.8 | 33 |
| 34 | 15 | 5.5 | 3 | 35 | 15,000 | 10.5 | 28 |
| 35 | 18 | 5.3 | 2.6 | 40 | 17,000 | 11.2 | 30.2 |
| 36 | 12 | 5.7 | 2.6 | 40 | 17,000 | 11.2 | 25.04 |