Codification of samples | Tensile strength (σ) (MPa) | Elongation at break (ε) (%) | Elastic Modulus (E) (MPa) | Energy to break (KJ/m2) | |
QsW1 | 98.82 ± 0.72 | 6.28 ± 0.07 | 2442.61 ± 198.63 | 195.371 ± 17.45 | |
QsSo10.5 | 48.43 ± 0.68 | 2.48 ± 0.07 | 2463.02 ± 185.32 | 25.907 ± 4.54 | |
QsSo11.0 | 44.74 ± 0.98 | 2.17 ± 0.09 | 2658.67 ± 219.63 | 20.864 ± 3.58 | |
QsSo15.0 | 35.02 ± 0.51 | 1.74 ± 0.05 | 3076.93 ± 275.53 | 11.559 ± 2.21 | |
QsPo10.5 | 12.25 ± 0.95 | 3.68 ± 0.07 | 660.52 ± 89.63 | 14.433 ± 1.08 | |
QsPo11.0 | 20.22 ± 0.85 | 6.45 ± 0.09 | 807.79 ± 97.45 | 45.643 ± 3.45 | |
QsPo15.0 | 19.82 ± 0.94 | 6.49 ± 0.07 | 816.14 ± 92.85 | 44.918 ± 2.18 | |
QsW2 | 107.55 ± 2.11 | 6.42 ± 0.02 | 3374.35 ± 212.28 | 239.737 ± 19.87 | |
QsSo20.5 | 76.1 ± 1.08 | 2.25 ± 0.03 | 4329.78 ± 282.81 | 39.637 ± 1.45 | |
QsSo21.0 | 79.5 ± 1.17 | 3.73 ± 0.02 | 3597.5 ± 231.78 | 83.865 ± 4.85 | |
QsSo25.0 | 89.34 ± 1.51 | 4.1 ± 0.02 | 3265.4 ± 210.48 | 101.022 ± 9.77 | |
QsPo20.5 | 75.28 ± 1.23 | 2.72 ± 0.05 | 3578.15 ± 222.22 | 44.054 ± 1.54 | |
QsPo21.0 | 46.51 ± 0.95 | 4.34 ± 0.04 | 2031.49 ± 182.28 | 68.573 ± 2.87 | |
QsPo25.0 | 80.16 ± 1.03 | 3.99 ± 0.09 | 3535.9 ± 242.44 | 86.524 ± 3.24 | |
QsW3 | 110.11 ± 2.23 | 4.72 ± 0.04 | 3291.74 ± 187.91 | 154.28 ± 4.69 | |
QsSo30.5 | 102.12 ± 2.35 | 4.5 ± 0.05 | 3878.32 ± 198.15 | 136.069 ± 4.84 | |
QsSo31.0 | 96.02 ± 1.23 | 4.55 ± 0.03 | 3962.47 ± 201.11 | 136.183 ± 4.12 | |
QsSo35.0 | 86.92 ± 1.12 | 5.42 ± 0.04 | 4083.23 ± 231.35 | 174.576 ± 5.14 | |
QsPo30.5 | 114.83 ± 2.34 | 3.62 ± 0.08 | 4464.65 ± 242.91 | 119.187 ± 3.87 | |
QsPo31.0 | 63.54 ± 0.93 | 2.64 ± 0.09 | 3217.24 ± 211.51 | 37.281 ± 2.69 | |
QsPo35.0 | 88.49 ± 1.03 | 2.76 ± 0.04 | 3974.87 ± 271.08 | 61.092 ± 3.01 |