Charging Materials | Chemical composition, wt.% | ||||||||||||
C | Si | Mn | Cr | Ni | V | W | Mo | Al | P | S | Ca | Fe | |
Scrap 1 | 0.3 | 0.30 | 1.08 | - | - | 0.007 | - | - | - | 0.030 | 0.022 | - | Bal. |
Scrap 2 | 0.1 | 0. 17 | 0.35 | - | - | 0.009 | - | - | - | 0.028 | 0.021 | - | Bal. |
LC Fe-Mn | 0.3 | 2.3 | 80.6 | - | - | 0.035 | - | - | - |
| - | 0.31 | 16.1 |
Fe-Si | - | 72.1 | 0.39 | - | - | 0.04 | - | - | 1.5 |
| - | 1.4 | 24.0 |
Fe-V | - | 2.5 | 0.26 | - | - | 77.5 | - | - | 3.03 |
| - | 0.2 | 16.0 |
LC Fe-Cr | - | 2.9 | 0.5 | 65 | - | 0.2 | - | - | 0.65 |
| - | - | 30 |
Fe-Mo | - | 2.0 | 0.21 | - | 0.36 | 0.15 | - | 55.55 | - |
| - | - | 41.5 |
Fe-W | - | - | 1.0 | - | - | 0.12 | 69 | 0.9 | - |
| - | 2.5 | 26 |
Ni alloy | - | 0.9 | 0.02 | - | 97.6 | 0.01 | - | - | - |
| - | 0.4 | 0.07 |