Matrix | Coating | Electrolyte composition | Process conditions | WCA | SA | Ref |
Copper | Ni/TiO2/ TMPSi | Plating solution: NiCl2 + H3BO3 + NiSO4 + SDS + TiO2 Modification: TMPSi | 80.7 A/dm2 (19.17 min), 50.5˚C + Surface modification | 151.6˚ | 6.2˚ | [22] |
mild steel | Ni/WS2 | NiSO4 + NiCl2 + H3BO3 + CTAB + WS2 + Saccharin | 4 A/dm2 (20 min), 40˚C | 158.3˚ | 7.7˚ | [100] |
Stainless steel | Cu/MoS2 | CuSO4 + H2SO4 + MoS2 + CTAB + thiourea | 50 mA/cm2 (2 min) | 158.2˚ | 1.8˚ | [101] |
Carbon steel | Ni/WC | NiSO4 + NiCl2 + H3BO3 + CTAB + WC | 6 A/dm2 (30 min), 40˚C | 164.3˚ | 0˚ | [102] |
Copper | Ni/PTFE | NiSO4 + NiCl2 + H3BO3 + PTFE particles | 100 mA/cm2 (15 min), 60˚C | ≈155˚ | - | [103] |