Matrix | Coating | Electrolyte composition | Process conditions | WCA | SA | Ref |
Be-Cu alloy | Cu Stearate | CuCl2 + HCl + stearic acid | 5 V (10 min) | 163˚ ± 4˚ | 1.7˚ ± 0.2˚ | [68] |
X90 steel | Cu-Zn | ZnSO4 + CuSO4 + NaOH + C4O6H4 KNa | 2 A/dm 2 (60 min) | 154.73˚ | 6.5˚ | [69] |
Mg alloy | Ce myristate | Ce(NO3)3 + myristic acid | 20 V (10 min) | 160.4˚ ± 0.7˚ | - | [70] |
Mg alloy | Ce stearate | Ce(NO3)3 + stearic acid | 30 V (10 min) | 158.4˚ ± 0.9˚ | 2˚ | [71] |
C45 steel | Fe | FeCl3 + palmitic acid + ethanol | 30 V (10 min) | 160.5˚ ± 0.5˚ | 2˚ ± 0.5˚ | [72] |
Copper | Al stearate | AlOx + stearic acid | 30 V (10 min) | 161˚ ± 1˚ | 2˚ ± 1˚ | [73] |