Properties | Fiber diameter | ||||
Group-1 | Group-2 | ||||
E1 | E3 | E4 | E6 | E2 | |
Average length (cm) | 0.1517 | 0.187 | 0.2751 | 1 | 0.4165 |
Elongation at break (%) | 0.000972*** | 0.427 | 0.004891** | 0.350 | 4.24e−07*** |
Load at break (N) | 4.407e−09*** | 0.307 | 0.005887** | 0.000976*** | 0.008426*** |
Tenacity (gf/Tex) | 0.000457*** | 0.0297* | 0.5724 | 0.000299*** | 0.01517* |
Tensile stress (MPa) | <2e−16*** | 0.0297* | <2e−16*** | 0.000292*** | <2e−16*** |
Young’s modulus (GPa) | 6.825e−16*** | 0.000267*** | 7.262e−14*** | 0.914 | 7.262e−14*** |
Aspect ratio (L/D) | <2.2e−16*** | 1.28e−06*** | 5.32e−11*** | 0.0245* | <2.2e−16*** |
Contact angle (˚) | 0.02345* | 0.127 | 0.6861 | 0.358 | 0.6485 |