Research | Filter name | Material | Pressure drop | Efficiency (%) | QF (Pa−1) | Note |
[10] | PAN 15 | Single layer of electrospun polyacrylonitrile nanofiber mat sandwiched between two activated carbon fiber mats. | 98 Pa | 89.8% | 0.0233 | Tested at 5.3 cm・s−1 with 300 nm polystyrene latex particles. |
[11] | N9 | Electrospun polyethylene oxide nanofiber layer on microfiber substrate. | 161 Pa | 85%* | 0.0118* | Tested at 5 cm・s−1 with NaCl particles from 50 to 480 nm. |
[12] | L | Electrospun nylon nanofiber layer on microfiber substrate. | 62 Pa | 60%* | 0.0147* | Tested at 5 cm・s−1 with NaCl particles from 50 to 500 nm. |
[13] | A3 | Nanoweb membrane obtained by meltblowing technique from polymers. | 119 Pa | 90% | 0.02 | Tested at 5.3 cm・s−1 with 0.3 μm DOP particles. |
Present study | C1 (0.1% mechanical) | Microfibrillated cellulose. | 55 Pa | 56%* | 0.0149* | Tested at 5.3 cm・s−1 with NaCl particles from 10 to 1000 nm. |
Present study | T1 (0.1% oxidized) | Microfibrillated cellulose. | 25Pa | 46%* | 0.0246* | Tested at 5.3 cm・s−1 with NaCl particles from 10 to 1000 nm. |