Samples | Young’s modulus | Ultimate Tensile Strength | Breaking Strength | Deformation at break | Maximum strain |
MPa | MPa | MPa | % | % | |
PLA Pure | 1291.0 ± 45 | 38.0 ± 3.1 | 4.0 ± 1.1 | 4.6 ± 0.6 | 15.0 ± 0.9 |
PLA 25TPS | 900.0 ± 198 | 8.0 ± 4.1 | 1.4 ± 0.6 | 1.4 ± 0.3 | 0.5 ± 0.5 |
PLA 35TPS | 850.0 ± 211 | 6.0 ± 3.5 | 1.1 ± 1.8 | 1.2 ± 0.1 | 2.2 ± 0.1 |
PLA 45TPS | 1618.0 ± 112 | 6.0 ± 2.6 | 0.6 ± 0.1 | 0.7 ± 0.1 | 1.3 ± 0.3 |