Glass systems | σ at 25˚C (S∙cm−1) | References |
62Li2O-38SiO2 and Li2S-SiO2 (thin film) | ~10−5 | A. Chandra et al. [52] Radhakrishna [53] |
0.35Li2O-0.75B2O3 (film) | 2.5 × 10−6 | M.R.S. Abouzari [51] |
50Li2O-50P2O5 | 2.8 × 10−9 | M. Ganguli et al. [54] |
0.3Li2O + 0.7GeO2 | 4.3 × 10−7 at 200˚C | K. Radhakrishnan et al. [55] |
Na2O-GeO2 | 2.3 × 10−5 | D. Ravaine [15] |
Na2O-SiO2 | 2.0 × 10−7 at 30˚C | D. Ravaine [15] |
Na2O-B2O3 | ~10−9 | R. Christensen et al. [56] |
Na2O-P2O5 | 5.6 × 10−11 | D. Ravaine [15] |