Experiments/fly ash/elements | Model parameters | Goodness of fit | |||||
α (mg∙kg−1∙h−1) | β kg∙kg−1 | R2 | ND | NSD | |||
Jar leaching | HA | As | 0.21 | 0.75 | 0.9873 | 9.3 | 16.0 |
Mo | 5.0 | 0.74 | 0.9593 | 8.8 | 14.9 | ||
Se | 0.37 | 2.09 | 0.9425 | 32.1 | 64.2 | ||
HB | As | 18.3 | 1.21 | 0.9620 | 4.1 | 5.2 | |
Mo | 0.81 | 0.46 | 0.8531 | 155.4 | 381.8 | ||
Se | 1.34 | 2.71 | 0.8285 | 15.5 | 19.3 | ||
MA | As | 2.4 × 104 | 2.40 | 0.8334 | 4.1 | 5.6 | |
Mo | 0.09 | 1.22 | 0.9163 | 35.4 | 56.3 | ||
Se | 0.40 | 9.48 | 0.8129 | 17.4 | 22.0 | ||
Long-term leaching | HA | As | 111 | 1.90 | 0.9003 | 6.86 | 8.21 |
Mo | 8.3 × 108 | 2.78 | 0.8589 | 0.86 | 1.24 | ||
Se | 252 | 5.04 | 0.9756 | 2.02 | 2.75 | ||
HB | As | 0.92 | 2.78 | 0.9777 | 35.01 | 58.39 | |
Mo | 175 | 0.40 | 0.9120 | 8.90 | 11.69 | ||
Se | 6.81 | 0.79 | 0.9777 | 9.30 | 16.33 | ||
MA | As | 0.57 | 2.17 | 0.9357 | 44.42 | 89.69 | |
Mo | 12.9 | 0.92 | 0.9686 | 6.47 | 9.06 | ||
Se | 1.38 | 3.96 | 0.9487 | 14.29 | 20.02 |