Composites | Density, g/cm3 | Hardness | Flexural strength, N/mm2 | UTS, N/mm^2 | % Elongation | TS@ 25°C (mm) | TS@ 50°C (mm) | TS@ 75°C (mm) |
Wood One |
|
|
|
|
|
|
|
|
W1S1 | 0.825 | 47 | 0.750 | 0.791 | 9.269 | 0.10 | 1.24 | 0.80 |
W1S2 | 0.970 | 40 | 0.699 | 0.294 | 13.490 | 0.14 | 0.05 | 0.52 |
W1S3 | 0.948 | 30 | 0.636 | 2.011 | 7.995 | 0.09 | 1.28 | 1.18 |
W1S4 | 0.877 | 52 | 4.703 | 4.327 | 14.410 | 1.58 | 0.14 | 0.15 |
W1S5 | 0.899 | 54 | 14.100 | 3.309 | 26.650 | 0.08 | 0.23 | 0.18 |
W1S6 | 0.864 | 48 | 6.629 | 3.326 | 15.600 | 0.07 | 0.31 | 0.22 |
Wood Two |
|
|
|
|
|
|
|
|
W2S1 | 0.936 | 50 | 3.066 | 0.653 | 10.710 | 0.05 | 0.42 | 0.10 |
W2S2 | 0.860 | 43 | 1.391 | 0.552 | 13.100 | 0.09 | 0.23 | 0.13 |
W2S3 | 0.962 | 41 | 0.988 | 0.644 | 8.938 | 0.10 | 0.18 | 0.30 |
W2S4 | 0.831 | 45 | 4.070 | 1.708 | 11.400 | 0.13 | 0.09 | 0.07 |
W2S5 | 0.867 | 45 | 4.472 | 2.790 | 9.552 | 0.18 | 0.10 | 0.07 |
W2S6 | 0.830 | 50 | 2.905 | 2.036 | 9.162 | 0.21 | 0.25 | 0.34 |
Wood Three |
|
|
|
|
|
|
|
|
W3S1 | 0.811 | 43 | 1.592 | 0.585 | 7.044 | 0.07 | 0.25 | 0.19 |
W3S2 | 0.801 | 42 | 2.477 | 1.676 | 11.250 | 0.04 | 0.15 | 0.07 |
W3S3 | 0.803 | 44 | 1.471 | 0.723 | 14.530 | 0.1 | 0.39 | 0.52 |
W3S4 | 0.867 | 49 | 4.971 | 1.950 | 12.024 | 0.05 | 0.15 | 0.15 |
W3S5 | 0.838 | 45 | 2.930 | 1.554 | 10.033 | 0.28 | 0.15 | 0.25 |
W3S6 | 0.924 | 55 | 3.189 | 1.435 | 10.900 | 0.3 | 0.19 | 0.25 |
Wood 4 |
|
|
|
|
|
|
|
|
W4S1 | 0.896 | 42 | 1.050 | 1.286 | 17.089 | 0.15 | 0.5 | 0.29 |
W4S2 | 1.058 | 56 | 1.975 | 1.620 | 7.910 | 0.2 | 0.48 | 0.09 |
W4S3 | 0.952 | 48 | 0.959 | 0.656 | 16.240 | 0.07 | 0.15 | 0.29 |
W4S4 | 0.870 | 50 | 0.769 | 1.169 | 5.764 | 0.07 | 0.59 | 0.33 |
W4S5 | 1.017 | 51 | 8.035 | 3.274 | 11.530 | 0.08 | 0.38 | 0.07 |
W4S6 | 0.876 | 47 | 1.051 | 0.796 | 25.180 | 0.13 | 0.28 | 0.10 |
Plastics |
|
|
|
|
|
|
|
|
PE | 0.590 | 46 | 8.341 | 5.966 | 24.490 |
|
|
|
PET | 1.140 | 62 | 19.950 | 14.820 | 6.121 |
|
|
|
C1 | 0.916 | 46 | 4.643 | 1.978 | 11.170 | 0.24 | 0.10 | 0.26 |
C2 | 0.928 | 51 | 11.190 | 3.557 | 9.766 | 0.12 | 0.03 | 0.32 |