Sample type | Sample code | Radioactivity concentration (Bq/kg−1) | ||
226Ra | 232Th | 40K | ||
Iron | F1 | 154.04 ± 4.89 | 162.28 ± 2.27 | 36.51 ± 2.17 |
F2 | 171.34 ± 5.12 | 135.63 ± 2.11 | 35.69 ± 2.0 | |
F3 | 224.53 ± 7.0 | 164.63 ± 2.22 | 46.29 ± 3.21 | |
F4 | 147.38 ± 4.56 | 115.62 ± 2.12 | 17.31 ± 1.12 | |
F5 | 169.16 ± 5.54 | 131.81 ± 2.0 | 27.58 ± 1.6 | |
Average (range) | 173.29 (147.38 ? 22,453) | 141.99 (115.62 - 164.63) | 32.68 (17.31 - 46.29) | |
Cooper | Cu1 | 1.23 ± 0.22 | 0.34 ± 0.02 | 11.94 ± .28 |
Cu2 | 3.26 ± 0.56 | 0.82 ± 0.03 | 45.82 ± 1.78 | |
Cu3 | 1.31 ± 0.08 | 0.98 ± 0.04 | 67.37 ± 2.28 | |
Cu4 | 5.58 ± 0.42 | 0.60 ± 0.03 | 16.37 ± 0.16 | |
Cu5 | 1.79 ± 0.42 | 0.26 ± 0.02 | 8.43 ± 0.42 | |
Average (RANGE) | 2.63 (1.23 - 5.58) | 0.60 (0.26 - 0.98) | 29.99 (8.43 - 67.37) | |
Aluminium | Al1 | 2.76 ± 0.76 | 0.54 ± 0.04 | 23.36 ± 1.14 |
Al2 | 1.56 ± 0.17 | 6.05 ± 1.50 | 36.99 ± 1.61 | |
Al3 | 3.08 ± 0.61 | 2.64 ± 0.86 | 27.91 ± 1.31 | |
Al4 | 7.24 ± 0.73 | 5,12 ± 1.15 | 55.49 ± 2.29 | |
Al5 | 5.23 ± 0.74 | 10.12 ± 2.22 | 64.58 ± 2.65 | |
Average (range) | 3.97 (1.56 - 7.24) | 4.89 (0.54 - 10.12) | 41.67 (23.36 - 64.580) | |
Wood | Wo1 | 1.30 ± 0.22 | 0.27 ± .03 | 10.81 ± .28 |
Wo2 | 10.75 ± 2.31 | 2.46 ± 0.04 | 7.79 ± 0.41 | |
Wo3 | 2.46 ± 0.65 | 3.51 ± 1.33 | 44.57 ± 2.01 | |
Wo4 | 5.56 ± 0.92 | 4.06 ± 0.34 | 72.26 ± 3.13 | |
Wo5 | 1.03 ± 0.03 | 5.25 ± 0.58 | 15.58 ± 0.81 | |
Average (range) | 4.22 (1.03 - 10.75) | 3.11 (0.27 - 5.25) | 30.20 (7.79 - 72.26) |