Annealing | Al50-Cu | Al25-Cu | Al10-Cu | Al50-Cu | Al25-Cu | Al10-Cu | Al50-Cu | Al25-Cu | Al10-Cu | Al50-Cu | Al25-Cu | Al10-Cu |
Vicker Hardness (HV) | Yield Strength (MPa) | Ultimate Strength (MPa) | Resistivity (μΩ cm) | |||||||||
As cast | 750.91 | 67.52 | 103.51 | --- | 82.4 | 653.2 | 82.8 | 194.5 | 653.2 | 2.792 | 6.601 | 4.278 |
500˚C | 786.19 | 298.68 | 79.23 | --- | 113.87 | 891 | 121.5 | 181.52 | 891 | 2.455 | 8.166 | 8.198 |
600˚C | 757.41 | 288.41 | 88.05 | --- | 232.3 | 1948.4 | 33 | 242.6 | 1948.4 | 3.834 | 3.886 | 34.874 |
700˚C | 788.97 | 181.69 | 89.01 | --- | 552.8 | 200 | 32.9 | 564.1 | 188.4 | 6.371 | 14.118 | 14.065 |
Pure Al |
| 20 |
|
| 90 |
|
|
|
|
| 2.82 |
|
Pure Cy |
| 72 |
|
| 314 |
|
|
|
|
| 1.71 |
|