n | Material | k1 k2 | htrans onset (μm) | Ftrans onset (μm) | Wtransition (mNμm/Δh) | Data Source |
1 | Zerodur Berkovich | 141.81 mN/μm3/2 189.24 | 1.54678 | 248.2246 | 86.8650 | Ceram Internat, Elsevier, 2016, 42, 12740, Figure 10 |
2 | Zerodur Cubecorner | 46.121 mN/μm3/2 62.230 | 3.33355 | 250.1074 | 96.4875 | |
3 | Fused SiO2 Berkovich | 1.5289 uN/nm3/2 1.8347 | 0.09016 | 1.19808 | 0.22610 | Hysitron Handbook |
4 | Fused SiO2 Cubecornera) | 0.4480 μN/nm3/2 0.5561 | 0.18883 | 1.12375 | 0.23926 | Int J Mater Res 2005 96, 1226 |
5 | Na2O-Al2O3-SiO2 Glass Berkovichb) | 1.8868 μN/nm3/2 2.2632 | 0.13679 | 3.10289 | 0.388391 | J Amer Ceram Soc 2018 101, 2930, Figure 2(A) |
6 | Na2O-Al2O3-SiO2 Glass Cubecorner | 0.4765 μN/nm3/2 0.6119 | 0.36145 | 3.08279 | 0.84159 | |
7 | 2C22 Steel stress-free, Berkovich | 45.814 mN/μm3/2 65.225 | 0.92967 | 34.20895 | 14.4435 | Procedia Engineering 2011, 10, 3528, Figure 1(b) |
8 | 2C22 Steel stress-free, Cubecorner | 9.1998 mN/μm3/2 13.139 | 2.38606 | 33.29274 | 11.35050 | |
9 | Nickel Berkovich | 127.56 mN/μm3/2 167.96 | 0.60051 | 52.75485 | 19.05449 | Philosophical Magazine 2016, 96, 3442 |
10 | Nickel Cubecorner | 25.124 mN/μm3/2 31.417 | 1.05640 | 26.24538 | 5.899987 | |
11 | Germaniμm Berkovich | 97.083 mN/μm3/2 128.58 | 0.27330 | 12.53433 | 4.377296 | Appl Phys Lett 2005, 86, 131907 |
12 | Germanium Cubecornerc) | 29.085 mN/μm3/2 |
|
|
| |
13 | Cu60Zr30Ti10d) Berkovich | 2.1803 μN/nm3/2 2.6791 | 0.15718 | 4.01683 | 0.969275 | Mater Sci Engin A 2006, 430, 350 |
14 | Vitreloy-105e) Cubecorner | 29.652 mN/μm3/2 36.139 | 2.53297 | 107.9909 | 28.29528 | Phil Mag 2006, 86, 5715-5728 |