| Mould Designation |
Mix Proportions |
W.P.F (%) |
Compressive Strength (MPa) |
K27 (m/s) M.N Akhtar et al. (2014) |
Ratios of Sample |
|||
| C (%) |
T.F.A (%) |
C.S (%) |
S.D (%) |
|||||
| Phase 1 |
|
|
|
|
|
|
|
|
| 00 TFASDRT 05 TFASDRT 10 TFASDRT 15 TFASDRT 20 TFASDRT |
10 10 10 10 10 |
70 70 70 70 70 |
20 15 10 05 00 |
00 05 10 15 20 |
1 1 1 1 1 |
3.56 3.84 4.25 4.19 3.89 |
4.603 × 10−7 4.310 × 10−7 3.911 × 10−7 3.618 × 10−7 3.240 × 10−7 |
1:7:2:0 1:7:1.5:0.5 1:7:1:1 1:7:0.5:1.5 1:7:0:2 |
| 00 TFASDRT 05 TFASDRT 10 TFASDRT 15 TFASDRT 20 TFASDRT |
10 10 10 10 10 |
60 60 60 60 60 |
30 25 20 15 10 |
00 05 10 15 20 |
1 1 1 1 1 |
3.74 4.06 4.47 4.35 4.15 |
2.937 × 10−7 2.815 × 10−7 2.525 × 10−7 2.330 × 10−7 2.180 × 10−7 |
1:6:3:0 1:6:2.5:0.5 1:6:2:1 1:6:1.5:1.5 1:6:1:2 |
| 00 TFASDRT 05 TFASDRT 10 TFASDRT 15 TFASDRT 20 TFASDRT |
10 10 10 10 10 |
50 50 50 50 50 |
40 35 30 25 20 |
00 05 10 15 20 |
1 1 1 1 1 |
4.05 4.35 4.61 4.53 4.41 |
4.777 × 10−7 4.462 × 10−7 4.238 × 10−7 4.068 × 10−7 4.020 × 10−7 |
1:5:4:0 1:5:3.5:0.5 1:5:3:1 1:5:2.5:1.5 1:5:2:2 |
| Phase 2 |
|
|
|
|
|
|
|
|
| 10 TFASDRT 15 TFASDRT 20 TFASDRT 25 TFASDRT 30 TFASDRT |
10 10 10 10 10 |
50 50 50 50 50 |
30 25 20 15 10 |
10 15 20 25 30 |
1 1 1 1 1 |
4.61 4.53 4.41 4.38 4.25 |
1.941 × 10−7 1.844 × 10−7 1.691 × 10−7 1.650 × 10−7 1.555 × 10−7 |
1:5:3:1 1:5:2.5:1.5 1:5:2:2 1:5:1.5:2.5 1:5:1:3 |
| 10 TFASDRT 15 TFASDRT 20 TFASDRT 25 TFASDRT 30 TFASDRT |
15 15 15 15 15 |
50 50 50 50 50 |
25 20 15 10 05 |
10 15 20 25 30 |
1 1 1 1 1 |
6.04 6.54 6.98 6.35 6.30 |
1.244 × 10−7 1.169 × 10−7 1.147 × 10−7 1.088 × 10−7 1.032 × 10−7 |
1:3.33:1.66:0.66 1:3.33:1.33:1 1:3.33:1:1.33 1:3.33:0.66:1.66 1:3.33:0.33:2 |
| 10 TFASDRT 15 TFASDRT 20 TFASDRT 25 TFASDRT 30 TFASDRT |
20 20 20 20 20 |
50 50 50 50 50 |
20 15 10 05 00 |
10 15 20 25 30 |
1 1 1 1 1 |
8.52 8.75 9.01 8.95 7.99 |
1.134 × 10−7 1.025 × 10−7 0.953 × 10−7 0.914 × 10−7 0.874 × 10−7 |
1:2.5:1:0.5 1:2.5:0.75:0.75 1:2.5:0.5:1 1:2.5:0:25:1.25 1:2.5:0:1.5 |