| Analysis | Unit | SS-EN 196-1, 2 and 3 | |
| MgO | % | 16.6 | |
| LOI | % | ?1.23 | |
| LOI compensated for S2− oxidation | % | 1.43 | |
| SO3 | % | 0.085 | |
| Sulfide | % | 1.33 | |
| Cl− | % | <0.01 | |
| Glass content | % | 99 | |
| Density | g/cm3 | 2.9 | |
| Specific surface area | m2/kg | 470 | |
| Moisture content | % | 0.09 | |
| Initial setting | Water content | % | 27.0 |
| Setting time | min | 210 | |
| Compressive strength | 7 days | MPa | 23.3 |
| 28 days | MPa | 50.4 | |