Properties | Magnesium | Aluminum | Iron |
Crystal Structure | HCP | FCC | BCC |
Standard Atomic Weight (g/mol) | 24.31 | 26.98 | 55.85 |
Density at 25˚C (g/cm3) | 1.738 | 2.70 | 7.87 |
Liquid Density at Melting Point (g/cm3) | 1.584 | 2.375 | 6.98 |
Melting Point (˚C) | 650 | 660 | 1536 |
Boiling Point (˚C) | 1091 | 2519 | 2862 |
Heat of Fusion (kJ/mol) | 8.48 | 10.71 | 13.81 |
Heat of Vaporization (kJ/mol) | 128 | 294 | 340 |
Heat Capacity at 25˚C (J/mol * K) | 24.869 | 24.2 | 25.1 |
Thermal Conductivity at 300 K (W/m * K) | 156 | 237 | 80.4 |
Thermal Expansion at 25˚C (µm/m * K) | 24.8 | 23.1 | 11.8 |
Young’s Modulus (GPa) | 45 | 70 | 211 |
Shear Modulus (GPa) | 17 | 26 | 82 |
Poisson Ratio | 0.29 | 0.35 | 0.29 |
Brinell Hardness (MPa) | 260 | 245 | 490 |