Entry | Temp. (˚C) | MMA:Initiator | Grafting Yield (%) | Homopolymer Yield (%) | Grafting Efficiency (%) | Mw (×106) | PDI |
1 | 23 | 50:1 | 1.1 | 61 | 0.06 | 1.3 | 2.3 |
2 | 40 | 50:1 | 0.63 | 51 | 0.63 | 1.0 | 1.9 |
3 | 50 | 50:1 | 16 | 88 | 0.98 | 1.0 | 2.6 |
4 | 60 | 50:1 | 7.3 | 68 | 1.2 | 1.5 | 2.0 |
5 | 70 | 50:1 | 2.0 | 89 | 0.086 | 1.3 | 2.1 |
6 | 50 | 100:1 | 13 | 64 | 1.4 | 2.5 | 2.6 |
7 | 50 | 150:1 | 11 | 52 | 1.7 | 2.1 | 2.6 |
8 | 50 | 200:1 | 9.6 | 63 | 1.0 | 2.7 | 2.9 |