| Sample | Ultimate Tensile Strength (UTS)—MPa | Modulus (E)—MPa | Max. Extension at UTS (mm) | Hardness (VH) |
| Base alloy | 226 | 188,857.25 | 0.71 | 241 |
| 1 | 227.39 | 23,258.98 | 0.483 | 412 |
| 2 | 233.98 | 26,591.76 | 0.484 | 434 |
| 3 | 256.34 | 22,436.65 | 0.6 | 402 |
| 4 | 269.21 | 24,306.08 | 0.62 | 458 |
| 5 | 195.62 | 21,920.02 | 0.79 | 458 |
| 6 | 208.21 | 21,043.17 | 0.53 | 423 |
| 7 | 245.83 | 20,919.35 | 1.31 | 354 |
| 8 | 262.47 | 20,342.65 | 1.35 | 471 |
| 9 | 218.30 | 15,037.89 | 2.62 | 458 |
| 10 | 281.11 | 19,991.65 | 0.74 | 513 |
| 11 | 230.71 | 15,256.17 | 0.63 | 498 |
| 12 | 223.86 | 18,976.56 | 0.45 | 484 |
| 13 | 213.77 | 17,788.58 | 0.51 | 458 |
| 14 | 145.65 | 13,245.32 | 0.039 | 434 |
| 15 | 169.89 | 14,898.58 | 1.59 | 354 |
| 16 | 200.18 | 20,649 | 0.47 | 458 |
| 17 | 226.72 | 18,859.83 | 0.72 | 354 |
| 18 | 186.35 | 18,082.91 | 0.54 | 372 |
| 19 | 179.84 | 20,655.68 | 0.46 | 363 |
| 20 | 168.0 | 23,254.84 | 0.4 | 336 |
| 21 | 111.99 | 18,472.36 | 0.44 | 318 |
| 22 | 230 | 23,463.87 | 0.52 | 310 |
| 23 | 157.36 | 21,572.99 | 0.05 | 327 |
| 24 | 186.83 | 24,010.95 | 0.049 | 318 |
| 25 | 173.18 | 19,597.46 | 0.47 | 382 |
| 26 | 150.57 | 22,225.90 | 0.42 | 266 |
| 27 | 217.43 | 24,306.94 | 0.51 | 279 |
| 28 | 213.90 | 24,762.38 | 0.63 | 336 |
| 29 | 239.59 | 21,078.47 | 0.64 | 382 |
| 30 | 231.45 | 20,195.65 | 0.62 | 336 |
| 31 | 223.25 | 20,051.78 | 0.61 | 345 |
| 32 | 178.61 | 20,472.81 | 0.62 | 363 |