Compounds | % Conversion | Ea (kJ/mole) | lnZ (1/s) |
Polystyrene | 3.0 | 179.74 | 25.35 |
| 5.0 | 197.76 | 28.87 |
| 8.0 | 195.70 | 28.59 |
| 12.0 | 197.22 | 28.97 |
| 18.0 | 198.01 | 29.24 |
| 26.0 | 200.36 | 29.83 |
Poly(4-methylstyrene) | 3.0 | 175.93 | 24.82 |
| 5.0 | 174.40 | 24.57 |
| 8.0 | 177.32 | 25.24 |
| 12.0 | 179.61 | 25.81 |
| 18.0 | 184.08 | 26.79 |
| 26.0 | 188.33 | 27.71 |
Poly(4-chlorostyrene) | 3.0 | 80.47 | 10.26 |
| 5.0 | 89.73 | 11.80 |
| 8.0 | 95.83 | 12.55 |
| 12.0 | 101.13 | 12.96 |
| 18.0 | 118.79 | 15.74 |
| 26.0 | 156.85 | 22.38 |
Poly(4-bromostyrene) | 3.0 | 241.31 | 37.26 |
| 5.0 | 223.45 | 33.89 |
| 8.0 | 211.87 | 31.74 |
| 12.0 | 207.98 | 31.06 |
| 18.0 | 201.95 | 30.02 |
| 26.0 | 197.61 | 29.32 |