Properties | Narrowest diameter | Average diameter | ||||||
E2 | T.E-2 | E4 | T.E-4 | E2 | T.E-2 | E4 | T.E-4 | |
Average length (cm) | 0.4165 | 0.3048 | 0.2751 | 0.5817 | - | - | - | - |
Elongation at break (%) | 4.24e−07*** | 7.84e−07*** | 0.004891** | 7.898e−07*** | - | - | - | - |
Load at break (N) | 0.008426*** | <2e−16*** | 0.005887** | 7.581e−07*** | - | - | - | - |
Tenacity (gf/Tex) | 0.01517* | 0.00015*** | 0.5734 | 1.132e−05*** | - | - | - | - |
Tensile stress (MPa) | <2e−16*** | <2e−16*** | <2e−16*** | <2e−16*** | - | - | - | - |
Young’s modulus (GPa) | 7.262e−14*** | 2.621e−11*** | 7.262e−14*** | 2.284e−11*** | - | - | - | - |
Aspect ratio (L/D) | <2.2e−16*** | <2.2e−16*** | 5.32e−11*** | 4.755e−11*** | - | - | - | - |
Contact angle (˚) | - | - | - | - | 0.6485 | 0.003818** | 0.6861 | 0.9309 |