| Breaking strength centinewton (cN) | Breaking strength l/dTex | Elongation at break mm | Elogation at break % | Breaking work/cN* mm | Breaking time/s | Yield strength/cN | Yield elogation/mm | Initial modulus cN/dTex |
Average value | 44.01 | 4.40 | 0.77 | 3.85 | 15.774 | 2.31 | 10.813 | 0.264 | 76.714 |
Maximum value | 114.79 | 11.48 | 1.36 | 6.81 | 60.95 | 4.08 | 51.31 | 0.81 | 179.8 |
Minimum value | 11.42 | 1.14 | 0.38 | 1.88 | 2.33 | 1.13 | 1.12 | 0.01 | 17.32 |
CV% | 47.37 | 47.37 | 30.67 | 30.67 | 70.93 | 30.64 | 100.805 | 69.68 | 51.54 |