Filament Composition | Run | Temperature (˚C) H1; H2 | Extrusion Speed (rpm) | Spooling Speed (rpm) | Avegrage Diameter (mm) | Standard Deviation (mm) |
100% HDPE 0% TPS | 1 | 220; 215 | 5 | 1.5 | 1.92 | 0.091 |
2 | 220; 215 | 5.5 | 2 | 1.72 | 0.016 | |
3 | 220; 215 | 6 | 2.5 | 1.25 | 0.026 | |
4 | 215; 210 | 5 | 2 | 1.7 | 0.036 | |
5 | 215; 210 | 5.5 | 2.5 | 1.69 | 0.014 | |
6 | 215; 210 | 6 | 1.5 | 1.93 | 0.079 | |
7 | 210; 200 | 5 | 2.5 | 1.43 | 0.065 | |
8 | 210; 200 | 5.5 | 1.5 | 1.59 | 0.049 | |
9 | 210; 200 | 6 | 2 | 1.81 | 0.070 | |
90% HDPE 10% TPS | 1 | 185; 180 | 4 | 1.5 | 1.86 | 0.139 |
2 | 185; 180 | 4.5 | 2 | 1.64 | 0.048 | |
3 | 185; 180 | 5 | 2.5 | 1.56 | 0.241 | |
4 | 180; 175 | 4 | 2 | 1.61 | 0.117 | |
5 | 180; 175 | 4.5 | 2.5 | 1.7 | 0.151 | |
6 | 180; 175 | 5 | 1.5 | 1.66 | 0.036 | |
7 | 175; 170 | 4 | 2.5 | 1.76 | 0.143 | |
8 | 175; 170 | 4.5 | 1.5 | 1.79 | 0.161 | |
9 | 175; 170 | 5 | 2 | 1.54 | 0.098 | |
1 | 180; 175 | 5 | 1.5 | 1.97 | 0.227 | |
2 | 180; 175 | 5.5 | 2 | 1.86 | 0.021 | |
3 | 180; 175 | 6 | 2.5 | 1.69 | 0.136 | |
4 | 175; 170 | 5 | 2 | 1.99 | 0.015 | |
80% HDPE 20% TPS | 5 | 175; 170 | 5.5 | 2.5 | 1.57 | 0.068 |
6 | 175; 170 | 6 | 1.5 | 1.92 | 0.060 | |
7 | 170; 165 | 5 | 2.5 | 1.65 | 0.133 | |
8 | 170; 165 | 5.5 | 1.5 | 1.77 | 0.132 | |
9 | 170; 165 | 6 | 2 | 1.88 | 0.016 | |
70% HDPE 30% TPS | 1 | 180; 175 | 4.5 | 1 | 1.81 | 0.227 |
2 | 180; 175 | 5 | 1.5 | 1.8 | 0.042 | |
3 | 180; 175 | 5.5 | 2 | 1.82 | 0.066 | |
4 | 175; 170 | 4.5 | 1.5 | 1.74 | 0.035 | |
5 | 175; 170 | 5 | 2 | 1.7 | 0.117 | |
6 | 175; 170 | 5.5 | 1 | 1.78 | 0.166 | |
7 | 170; 165 | 4.5 | 2 | 1.74 | 0.030 | |
8 | 170; 165 | 5 | 1 | 1.99 | 0.136 | |
9 | 170; 165 | 5.5 | 1.5 | 1.6 | 0.120 | |
60% HDPE 40% TPS | 1 | 170; 165 | 4.5 | 1 | 1.81 | 0.230 |
2 | 170; 165 | 5 | 1.5 | 1.8 | 0.192 | |
3 | 170; 165 | 5.5 | 2 | 1.82 | 0.216 | |
4 | 165; 160 | 4.5 | 1.5 | 1.74 | 0.187 | |
5 | 165; 160 | 5 | 2 | 1.7 | 0.131 | |
6 | 165; 160 | 5.5 | 1 | 1.78 | 0.169 | |
7 | 160; 155 | 4.5 | 2 | 1.74 | 0.163 | |
8 | 160;155 | 5 | 1 | 1.99 | 0.140 | |
9 | 160; 155 | 5.5 | 1.5 | 1.6 | 0.137 |