Test Parameters | Reference | K1 | K2 | K3 | K4 | |
Moving Die Reometer, 191˚C, 15 min | ML (dNm) | 3.09 | 2.15 | 2.13 | 2.30 | 2.08 |
MH (dNm) | 13.21 | 9.18 | 8.84 | 9.06 | 10.83 | |
ts2 (min) | 01:09 | 01:13 | 01:13 | 01:18 | 01:21 | |
t90 (min) | 08:32 | 06:41 | 05:18 | 07:07 | 08:39 | |
Mooney Viscosity, 135˚C | ML1 + 4 | 59.51 | 45.32 | 44.10 | 45.37 | 55.31 |
T5 (min) | 16:46 | 17:59 | 21:25 | 18:07 | 14:19 | |
Physico-Mechanical, 170˚C 15 min | Tensile Strength (kg/cm2) | 160.78 | 148.95 | 168.78 | 157.9 | 159.06 |
Elongation, % | 612.14 | 604.87 | 699.32 | 703.26 | 510.44 | |
%300 Modulus (kg/cm2) | 61.12 | 51.52 | 43.41 | 41.55 | 79.77 | |
| Hardness (Shore A) | 62.80 | 56.20 | 54.10 | 57.60 | 64.20 |