| CAL | GAN_M | GAN_C | SOA | MLak1 | MLak2 | MLak3 | MLak4 | JES |
Mg* | 50.5 ± 1.8 | 2990 ± 105 | 2879 ± 101 | 2878 ± 91 | 11.3 ± 0.2 | 32.3 ± 1.0 | 126 ± 4 | 166 ± 6 | 240 ± 10 |
Ca* | 17.5 ± 0.5 | 4585 ± 148 | 4991 ± 177 | 4568 ± 122 | 10.5 ± 0.1 | 15.9 ± 0.5 | 42.3 ± 1.7 | 148 ± 6 | 79.5 ± 2.5 |
V | 8.21 ± 0.25 | 2.29 ± 0.03 | 2.25 ± 0.09 | 2.03 ± 0.10 | 4.19 ± 0.11 | 5.59 ± 0.16 | 4.81 ± 0.27 | 0.92 ± 0.05 | 6.08 ± 0.21 |
Ca | 3.58 ± 0.10 | 0.93 ± 0.03 | 0.67 ± 0.05 | 0.75 ± 0.01 | | 2.09 ± 0.05 | | 4.91 ± 0.08 | |
Mn | 242 ± 5 | 119 ± 4 | 104 ± 3 | 145 ± 3 | 101 ± 1 | 58.2 ± 1.6 | 132 ± 3 | 10662 ± 17.03 | 128 ± 4 |
Fe | 4440 ± 100 | 2443 ± 79 | 2678 ± 49 | 2929 ± 88 | 1861 ± 26 | 1653 ± 24 | 231 ± 4 | 1712 ± 33 | 199 ± 10 |
Co | 1.05 ± 0.02 | 0.64 ± 0.02 | 0.73 ± 0.02 | 0.97 ± 0.03 | 0.58 ± 0.04 | 0.55 ± 0.04 | 0.22 ± 0.02 | 6.66 ± 0.06 | 0.18 ± 0.01 |
Ni | | | | | 6.97 ± 0.07 | | | 125 ± 2 | |
Cu | | | | | 11.9 ± 0.4 | | | 422 ± 9 | |
Zn | 21.4 ± 0.7 | | | | 10.5 ± 0.4 | | | 633 ± 12 | |
As | 1.65 ± 0.15 | 2.44 ± 0.19 | 1.83 ± 0.16 | | 4.40 ± 0.20 | | 1.53 ± 0.37 | 1.83 ± 0.15 | 1.66 ± 0.23 |
Se | | | | | | | | | |
As | | | | | | | | | |
Be | 0.16 ± 0.02 | | | 0.074 ± 0.016 | | 0.11 ± 0.01 | | 0.084 ± 0.012 | |
Al | 4813 ± 202 | 1161 ± 37 | 1218 ± 53 | 1162 ± 52 | 1756 ± 27 | 2768 ± 121 | 218 ± 10 | 215 ± 11 | 223 ± 11 |
Sr | 249 ± 2 | 57.1 ± 0.8 | 57.6 ± 0.7 | 58.2 ± 0.3 | 130 ± 2 | 225 ± 1 | 795 ± 7 | 597 ± 1 | 1530 ± 17 |
Mo | 1.48 ± 0.04 | 0.91 ± 0.02 | 0.71 ± 0.03 | 1.77 ± 0.05 | 1.17 ± 0.02 | 27.2 ± 0.1 | 1.87 ± 0.05 | 16.2 ± 0.2 | 2.71 ± 0.01 |
Ag | | | | | | | | | |
Sn | | | | | | | 6.00 ± 0.33 | 12.7 ± 0.2 | |
Ba | 48.1 ± 0.7 | 49.1 ± 0.1 | 52.0 ± 0.5 | 54.1 ± 0.6 | 42.0 ± 0.2 | 23.3 ± 0.2 | 30.8 ± 0.2 | 184 ± 4 | 41.5 ± 0.3 |
Pt | | | | | | | | | |
Hg | | | | | | | | 0.51 ± 0.01 | |
Tl | 0.060 ± <0.007 | 0.053 ± 0.009 | 0.049 ± 0.005 | 0.048 ± 0.008 | | 0.055 ± 0.003 | 0.044 ± 0.014 | 4.02 ± 0.04 | 0.042 ± <0.007 |
Pb | 2.43 ± 0.09 | 0.76 ± 0.02 | 0.45 ± 0.01 | 0.44 ± 0.03 | 1.10 ± 0.04 | 0.94 ± 0.03 | 1.57 ± 0.03 | 3.22 ± 0.05 | 0.24 ± 0.01 |
Th | 0.83 ± 0.03 | | | 0.61 ± 0.06 | | 0.62 ± 0.03 | 0.67 ± 0.01 | 1.31 ± 0.05 | 0.60 ± 0.02 |
U | 0.28 ± 0.01 | 0.075 ± 0.003 | 0.082 ± <0.007 | 0.075 ± 0.005 | 0.19 ± 0.02 | 0.35 ± 0.01 | 0.41 ± 0.01 | 0.043 ± 0.006 | 0.61 ± 0.01 |