Year | Average Micronaire | ||
2.5 mm/d (Low) | 5.1 mm/d (Medium) | 7.6 mm/d (High) | |
1996 | 4.804 a | 4.590 b | 4.429 c |
1997 | 4.792 a | 4.799 a | 4.721 a |
1998 | 4.525 a | 4.119 a | 3.982 a |
1999 | 4.817 a | 4.875 a | 4.825 a |
Average | 4.732 a | 4.598 b | 4.494 b |
Year | Average Fiber Length Uniformity (%) | ||
2.5 mm/d (Low) | 5.1 mm/d (Medium) | 7.6 mm/d (High) | |
1996 | 82.333 ab | 82.667 a | 81.771 b |
1997 | 82.794 b | 83.400 a | 83.750 a |
1998 | 81.908 a | 81.442 a | 81.528 a |
1999 | 82.917 a | 83.453 a | 83.642 a |
Average | 82.488 a | 82.740 a | 82.673 a |
Year | Average Fiber Strength (grams/tex) | ||
2.5 mm/d (Low) | 5.1 mm/d (Medium) | 7.6 mm/d (High) | |
1996 | 31.042 a | 30.542 a | 29.625 b |
1997 | 30.842 c | 30.575 b | 30.535 a |
1998 | 29.283 a | 28.859 a | 28.671 a |
1999 | 28.950 a | 29.152 a | 28.231 a |
Average | 30.202 a | 29.957 a | 29.458 b |