Samples | Flexion (bars) | Compression (bars) | Wear (mm) | Water Absorption (%) | Density (g/cm3) | Ultrasonic (m/s) | Whiteness index |
Har 1 | 200 | 620 | 36 | 0.9 | 2.46 | 4918 | 80.12 |
Har 2 | 205 | 620 | 37 | 0.93 | 2.45 | 4915 | 81.11 |
Har 3 | 205 | 630 | 37 | 0.92 | 2.5 | 4917 | 81.2 |
Har 4 | 210 | 650 | 36 | 0.94 | 2.5 | 4910 | 80.27 |
Har 5 | 205 | 644 | 36 | 0.95 | 2.5 | 4908 | 80.24 |
Har 6 | 205 | 680 | 34 | 0.14 | 2.5 | 4915 | 80.31 |
Har 7 | 212 | 685 | 34 | 0.15 | 2.5 | 4905 | 80.28 |
Har 8 | 215 | 695 | 33 | 0.17 | 2.51 | 4904 | 80.1 |
Har 9 | 216 | 700 | 33 | 0.2 | 2.52 | 4908 | 80.02 |
Average value | 208 | 658 | 35 | 0.59 | 2.49 | 4911 | 80.41 |
Hme 1 | 104 | 540 | 32 | 0.9 | 2.56 | 4865 | 79.23 |
Hme 2 | 105 | 550 | 32 | 0.94 | 2.55 | 4865 | 72.11 |
Hme 3 | 105 | 570 | 31 | 0.95 | 2.5 | 4865 | 73.28 |
Hme 4 | 106 | 570 | 31 | 0.94 | 2.5 | 4880 | 73.27 |
Hme 5 | 105 | 590 | 30 | 0.94 | 2.52 | 4833 | 73.74 |
Hme 6 | 105 | 600 | 30 | 0.95 | 2.54 | 4874 | 73.11 |
Hme 7 | 108 | 610 | 29 | 0.95 | 2.55 | 4880 | 73.78 |
Hme 8 | 108 | 620 | 29 | 1 | 2.54 | 4881 | 73.33 |
Hme 9 | 110 | 630 | 29 | 1 | 2.55 | 4882 | 73.68 |
Average value | 106 | 586 | 30 | 0.95 | 2.53 | 4870 | 73.95 |
Jer 1 | 200 | 760 | 28 | 0.6 | 2.5 | 5230 | 71.25 |
Jer 2 | 200 | 750 | 26 | 0.5 | 2.5 | 5235 | 70.13 |
Jer 3 | 201 | 770 | 27 | 0.62 | 2.5 | 5215 | 70.42 |
Jer 4 | 201 | 850 | 26 | 0.75 | 2.5 | 5250 | 70 |
Jer 5 | 202 | 810 | 26 | 1.05 | 2.52 | 5240 | 70.1 |
Jer 6 | 201 | 860 | 28 | 1.14 | 2.52 | 5220 | 70.5 |
Jer 7 | 204 | 940 | 27 | 1.35 | 2.52 | 5230 | 70.4 |
Jer 8 | 204 | 950 | 27 | 1.6 | 2.53 | 5240 | 70.2 |
Jer 9 | 205 | 990 | 28 | 1.6 | 2.53 | 5238 | 70.2 |
Average value | 202 | 853 | 27 | 1.02 | 2.51 | 5233 | 70.36 |