S/N | specimen | Bar diameter (mm) | Former diameter (3d + 3) mm | Observations | Decision of EN 10080:2005 Provisions |
1 | S1 | 10 | 33 | No Cracks Observed | Satisfactory |
2 | S2 | 10 | 33 | Cracks Observed | Unsatisfactory |
3 | S3 | 10 | 33 | Total breakage | Unsatisfactory |
4 | S4 | 10 | 33 | No Cracks Observed | Satisfactory |
5 | S5 | 10 | 33 | No Cracks Observed | Satisfactory |
6 | S6 | 10 | 33 | No Cracks Observed | Satisfactory |
7 | S7 | 10 | 33 | Cracks Observed | Unsatisfactory |
8 | S8 | 10 | 33 | No Cracks Observed | Satisfactory |
9 | S9 | 10 | 33 | No Cracks Observed | Satisfactory |
10 | S10 | 10 | 33 | No Cracks Observed | Satisfactory |
11 | S11 | 10 | 39 | No Cracks Observed | Satisfactory |
12 | S12 | 10 | 39 | No Cracks Observed | Satisfactory |
13 | S13 | 10 | 39 | No Cracks Observed | Satisfactory |
14 | S14 | 10 | 39 | No Cracks Observed | Satisfactory |
15 | S15 | 10 | 39 | No Cracks Observed | Satisfactory |
16 | S16 | 10 | 39 | Cracks Observed | Unsatisfactory |
17 | S17 | 10 | 39 | Cracks Observed | Unsatisfactory |
18 | S18 | 10 | 39 | No Cracks Observed | Satisfactory |
19 | S19 | 10 | 39 | No Cracks Observed | Satisfactory |
20 | S20 | 10 | 39 | No Cracks Observed | Satisfactory |
21 | S21 | 14 | 45 | No Cracks Observed | Satisfactory |
22 | S22 | 14 | 45 | No Cracks Observed | Satisfactory |
23 | S23 | 14 | 45 | No Cracks Observed | Satisfactory |
24 | S24 | 14 | 45 | No Cracks Observed | Satisfactory |