| Powdera | Mean particle size (μm) | Oxygen content (%) | Oxide layer thickness (nm) | Flowability (s/50g) | ρapp (g/cm3) | ρtap (g/cm3) | Ref. |
| Ti-6Al-4V powder |
|
|
|
|
|
| Simonelli et al. [56] |
| As-received (PA) |
|
|
| 32.4 ± 0.5 |
|
|
|
| Simply mixed 1 |
|
|
|
|
|
|
|
| Simply mixed 2 |
|
|
| 40.0 ± 1.0 |
|
|
|
| Satellite-mixed |
|
|
| 36.12 ± 0.07 |
|
|
|
| Ti-6Al-4V powder |
|
|
|
|
|
| Vert et al. [57] |
| As-received (HDH) | 90 - 340 | 3017 ppm |
| 50 | 1.89 | 2.32 |
|
| After ICPb treatment | 70 - 200 | 2100 ppm |
| 23 | 2.74 | 2.95 |
|
| Ti powder |
|
|
|
|
|
| Ding et al. [60] |
| As-received (HDH) | 28.6 | 0.35 | 6 |
|
|
|
|
| FBRb treatment, at 450˚C | 30.5 | 0.39 | 10 | 35.2 ± 0.3 |
|
|
|
| FBR treatment, at 500˚C | 32.5 | 0.50 |
| 32.6 ± 0.2 |
|
|
|
| FBR treatment, at 550˚C | 33.9 | 0.80 |
| 40.0 |
|
|
|
| FBR treatment, at 600˚C | 31.8 | 1.50 | 20 | 73.5 ± 0.5 |
|
|
|