| Value of the indicator | ||||||||||
U, V | 0.05 | 0.1 | 0.2 | 0.3 | 0.4 | 0.5 | 0.6 | 0.7 | 0.8 | 0.9 | 1 |
| Lignin, characterized by CaCl2 water solution content of 25 wt.% | ||||||||||
R, kΩ | 200 | 197 | 191 | 184 | 197 | 175 | 173 | 171 | 169 | 169 | 167 |
ρ·10−2, S/cm | 1 | 1.02 | 1.05 | 1.09 | 1.02 | 1.14 | 1.16 | 1.17 | 1.18 | 1.18 | 1.2 |
| Lignin, characterized by CaCl2 water solution content of 33 wt.% | ||||||||||
R, kΩ | 40.1 | 39.8 | 39.2 | 38.6 | 38.2 | 37.5 | 37 | 36.6 | 36.2 | 35.8 | 35.7 |
ρ·10−2, S/cm | 4.99 | 5.03 | 5.1 | 5.18 | 5.24 | 5.33 | 5.41 | 5.46 | 5.52 | 5.59 | 5.6 |
| Lignin, characterized by CaCl2 water solution content of 50 wt.% | ||||||||||
R, kΩ | 4.75 | 4.7 | 4.6 | 4,5 | 4.44 | 4.35 | 4.25 | 4.1 | 4.1 | 4 | 3.9 |
ρ·10−2, S/cm | 42.1 | 42.6 | 43.5 | 44.4 | 45 | 46 | 47.1 | 47.8 | 48.8 | 50 | 51.3 |
| Lignin, characterized by CaCl2 water solution content of 60 wt.% | ||||||||||
R, kΩ | 1 | 1.1 | 1 | 1 | 0.98 | 0.95 | 0.93 | 0.91 | 0.89 | 0.88 | 0.87 |
ρ·10−2, S/cm | 200 | 182 | 200 | 200 | 204 | 211 | 215 | 220 | 225 | 227 | 230 |