Schedule | Deformation Temperature (T) | Soaking Time (t) | True Strain ( ) | Strain Rate ( ) |
I | 950˚C | 1200 s | −0.5 mm/mm | 0.05 s−1 |
0.1 s−1 | ||||
0.5 s−1 | ||||
II | 900˚C | 1200 s | −0.5 mm/mm | 0.05 s−1 |
0.1 s−1 | ||||
0.5 s−1 | ||||
III | 850˚C | 1200 s | −0.5 mm/mm | 0.05 s−1 |
0.1 s−1 | ||||
0.5 s−1 | ||||
IV | 800˚C | 1200 s | −0.5 mm/mm | 0.05 s−1 |
0.1 s−1 | ||||
0.5 s−1 |