Measure | Masterbatch | Strength 100a (N) | Ultimate length (mm) | Elongation at break (%) | Strength at break (N) | Stress at break (MPa) | Modulus at break (MPa) | Modulus 100b (MPa) |
Mean value | A | 17.6 | 61.2 | 245 | 36.1 | 2.44 | 0.98 | 1.19 |
B | 21.0 | 79.7 | 319 | 56.5 | 3.82 | 1.19 | 1.42 | |
C | 22.5 | 65.4 | 262 | 44.6 | 3.02 | 1.16 | 1.52 | |
STD | A | 3.5 | 9.2 | 37 | 10.4 | 0.70 | 0.17 | 0.23 |
B | 2.4 | 9.0 | 36 | 9.5 | 0.64 | 0.10 | 0.16 | |
C | 3.6 | 6.7 | 27 | 4.8 | 0.33 | 0.19 | 0.24 | |
CoV (%) | A | 19.9 | 15.0 | 15.1 | 28.8 | 28.7 | 17.3 | 19.3 |
B | 11.4 | 11.3 | 11.3 | 16.8 | 16.8 | 8.4 | 11.3 | |
C | 16 | 10.2 | 10.3 | 10.8 | 10.9 | 16.4 | 15.8 |