Mass mat | Lattice parameter l (nm) | Frequency ω (THz) |
Yb2O3: 27.23 × 10−26 kg | 1.06 | 25.38 at 12.1 mW |
|
| 25.31 at 25 mW |
|
| 26.43 at 12.1 mW |
|
| 26.30 at 25 mW |
|
| 27.78 at 12.1 mW |
|
| 27.81 at 25 mW |
LaAlO3: 15.61 × 10−26 kg | 0.79 (average) | 14.65 at 12.1 mW |
|
| 14.62 at 25 mW |
|
| 15.99 at 12.1 mW |
|
| 15.94 at 25 mW |