Sample (x) | BMT (h) | I.S, (mm/s) | Q.S. (mm/s) | BHF (T) | Abundance (%) | Phase | ||
0.1 | 0 | 0.26 | −0.22 | 50.84 | 98.75 | α-Fe2O3 | ||
|
| 0.14 | 0.35 |
| 1.23 | <7 nm | ||
| 2 | 0.26 | −0.21 | 51.15 | 65.18 | α-Fe2O3 | ||
|
| 0.26 | −0.20 | 49.65 | 34.82 | Gd:Fe2O3 | ||
| 4 | 0.26 | −0.20 | 51.4 | 35.05 | α-Fe2O3 | ||
|
| 0.26 | −0.61 | 50.33 | 33.25 | Gd:Fe2O3 | ||
|
| 0.26 | −0.17 | 48.27 | 31.70 | Gd:Fe2O3 | ||
| 8 | 0.27 | −0.20 | 51.00 | 63.13 | α-Fe2O3 | ||
|
| 0.26 | −0.17 | 48.27 | 34.45 | Gd:Fe2O3 | ||
|
| 0.10 | 0.27 |
| 2.42 | GdFeO3 | ||
| 12 | 0.27 | −0.20 | 50.90 | 44.29 | α-Fe2O3 | ||
|
| 0.26 | −0.11 | 47.30 | 53.58 | Gd:Fe2O3 | ||
|
| 0.32 | 0.57 |
| 2.13 | GdFeO3 | ||
0.3 | 0 | 0.26 | −0.21 | 50.87 | 97.55 | α-Fe2O3 | ||
|
| 0.09 | 0.32 |
| 2.45 | <7 nm | ||
| 2 | 0.26 | −0.20 | 51.17 | 68.03 | α-Fe2O3 | ||
|
| 0.25 | −0.18 | 49.01 | 30.02 | Gd:Fe2O3 | ||
|
| 0.18 | 0.47 |
| 1.95 | GdFeO3 | ||
| 4 | 0.26 | −0.19 | 51.13 | 55.51 | α-Fe2O3 | ||
|
| 0.26 | −0.22 | 48.68 | 35.63 | Gd:Fe2O3 | ||
|
| 0.19 | 0.72 |
| 8.86 | GdFeO3 | ||
| 8 | 0.26 | −0.20 | 51.03 | 35.95 | α-Fe2O3 | ||
|
| 0.26 | −0.17 | 48.58 | 31.91 | Gd:Fe2O3 | ||
|
| 0.21 | 0.88 |
| 32.14 | GdFeO3 | ||
| 12 | 0.26 | −0.20 | 51.08 | 31.13 | α-Fe2O3 | ||
|
| 0.20 | −0.22 | 47.33 | 27.25 | Gd:Fe2O3 | ||
|
| 0.21 | 0.79 |
| 41.62 | GdFeO3 | ||
0.5 | 0 | 0.26 | −0.22 | 50.78 | 98.26 | α-Fe2O3 | ||
|
| 0.09 | 0.35 |
| 1.74 | <7 nm | ||
| 2 | 0.26 | −0.18 | 51.32 | 50.94 | α-Fe2O3 | ||
|
| 0.28 | −0.18 | 49.35 | 42.94 | Gd:Fe2O3 | ||
|
| 0.08 | 0.26 |
| 6.12 | GdFeO3 | ||
| 4 | 0.26 | −0.18 | 51.33 | 35.26 | α-Fe2O3 | ||
|
| 0.27 | −0.18 | 49.54 | 37.04 | Gd:Fe2O3 | ||
|
| 0.20 | 0.87 |
| 27.70 | GdFeO3 | ||
| 8 | 0.26 | −0.19 | 50.89 | 27.49 | α-Fe2O3 | ||
|
| 0.26 | −0.06 | 48.13 | 36.65 | Gd:Fe2O3 | ||
|
| 0.22 | 0.91 |
| 35.86 | GdFeO3 | ||
| 12 | 0.26 | −0.19 | 51.01 | 28.15 | α-Fe2O3 | ||
|
| 0.25 | −0.05 | 48.87 | 34.80 | Gd:Fe2O3 | ||
|
| 0.21 | 0.94 |
| 37.0 | GdFeO3 | ||
0.7 | 0 | 0.26 | −0.21 | 50.95 | 98.33 | α-Fe2O3 | ||
|
| 0.11 | 0.32 |
| 1.67 | <7 nm | ||
| 2 | 0.26 | −0.20 | 51.28 | 63.19 | α-Fe2O3 | ||
|
| 0.24 | −0.18 | 49.14 | 28.38 | Gd:Fe2O3 | ||
|
| 0.03 | 0.52 |
| 8.43 | GdFeO3 | ||
| 4 | 0.26 | −0.18 | 51.18 | 58.69 | α-Fe2O3 | ||
|
| 0.11 | −0.16 | 47.76 | 24.47 | Gd:Fe2O3 | ||
|
| 0.10 | 0.63 |
| 16.85 | Gd:Fe2O3 | ||
| 8 | 0.26 | −0.19 | 51.05 | 32.57 | α-Fe2O3 | ||
|
| 0.24 | −0.15 | 48.26 | 30.36 | Gd:Fe2O3 | ||
|
| 0.18 | 0.93 |
| 37.06 | GdFeO3 | ||
| 12 | 0.27 | −0.15 | 50.54 | 23.94 | α-Fe2O3 | ||
|
| 0.27 | −0.06 | 47.93 | 34.42 | Gd:Fe2O3 | ||
|
| 0.19 | 0.96 |
| 41.64 | GdFeO3 | ||
Errors: |
| ±0.01 | ±0.02 | ±0.5 | ±0.5 |
| ||