Sample | weight before test (g) | weight after test (g) | rate of corrosion ×10−5 (g/cm2∙min) |
Bare substrate | 9.0975 | 5.7162 | 19.57 |
TiO2 | 9.0945 | 6.3181 | 16.07 |
WT (0.5) | 9.0990 | 6.2845 | 16.29 |
WT (1) | 9.0504 | 6.3375 | 15.70 |
WT (2) | 9.0725 | 6.2969 | 16.06 |
WT (4) | 9.0458 | 6.3673 | 15.50 |
WO3 | 9.0741 | 6.2388 | 16.41 |