Coating | weight before test (g) | weight after test (g) | Rate of corrosion ×105 (g/cm2∙min) |
Bare substrate | 9.0930 | 6.9609 | 12.339 |
TiO2 | 9.0989 | 7.4859 | 9.334 |
WT (0.5) | 9.0942 | 7.5393 | 8.998 |
WT (1) | 9.0778 | 7.5759 | 8.692 |
WT (2) | 9.0733 | 7.4347 | 9.483 |
WT (4) | 9.0635 | 7.4322 | 9.440 |
WO3 | 9.1027 | 7.3400 | 10.201 |