| Parameters | Value | SI Unit |
| Density | 2.66 | g/cm3 |
| Ultimate Tensile Strength | 290 | MPa |
| Tensile Yield Strength | 131 | MPa |
| Compressive yield Strength | 131 | Mpa |
| Poisson’s Ratio | 0.33 |
|
| Young’s Modulus | 71 | Gpa |
| Shear Modulus | 26.7 | Gpa |
| Shear strength | 170 | Mpa |
| Thermal Conductivity | 121 | W/m∙K |
| Fatigue Strength | 130 | Mpa |
| Coefficient of thermal expansion | 204 | μm/m∙K |
| Elongation at break | 3.5% |
|
| Heat of fusion | 389 | J/g |
| Specific Heat Capacity | 0.963 | J/g∙˚C |
| Melting Point | 574-582 | ˚C |
| Melting temperature | 649-760 | ˚C |
| Casting temperature | 635-704 | ˚C |