Heat treatment [˚C] | Thickness [mm] | Ultimate strength [MPa] | Yield Strength [MPa] | %Elongation | Impact strength [J] | Hardness HV |
As-cast | 5 | 675 | 620 | 7.9 | 11 | 280 |
As-cast | 10 | 674 | 615 | 8 | 28 | 260 |
As-cast | 15 | 660 | 600 | 10 | 29 | 250 |
900/375 | 5 | 1056 | 996 | 3.7 | 31 | 396 |
900/375 | 10 | 1006 | 927 | 4.9 | 32 | 351 |
900/375 | 15 | 963 | 950 | 4 | 37 | 331 |
810/375 | 5 | 896 | 849 | 6.8 | 34 | 344 |
810/375 | 10 | 867 | 707 | 6.7 | 40 | 317 |
810/375 | 15 | 746 | 650 | 6.6 | 43 | 298 |