Boron waste ratio (%, w/w) | Drying shrinkage (%) | Firing shrinkage (%) | Weight loss (%) | Bulk density (g/cm3) | Water absorption (%) | Drying strength (N/mm2) | Firing strength (N/mm2) |
0 | 0.29 | 1.10 | 10.14 | 1.82 | 17.40 | 2.89 | 13.69 |
2 | 0.50 | 1.14 | 10.54 | 1.81 | 17.34 | 3.17 | 13.86 |
4 | 0.66 | 1.20 | 10.87 | 1.83 | 14.97 | 3.24 | 13.87 |
6 | 0.87 | 1.82 | 11.19 | 1.84 | 14.56 | 3.42 | 15.16 |
8 | 0.31 | 1.93 | 11.45 | 1.88 | 13.82 | 3.67 | 16.43 |
10 | 0.59 | 2.12 | 11.64 | 1.77 | 16.15 | 3.72 | 15.87 |
TS 202 | - | - | - | min. 1.70 | max. 20.00 | - | min. 15.00 |