Glass sample code | Starting oxide mixtures mol % | ρ (g∙cm−3) (±0.01) | Molar mass (g∙mol−1) | Molar volume (Å3) VoM = M/[ρ NA No*] | Calculated oxygen radius (Å) rcal (O2−) | |||
P2O5 | CaO | Na2O | TiO2 | |||||
48T05 | 48 | 30 | 21.5 | 0.5 | 2.57 | 98,719 | 21.81 | 1397 |
48T10 | 48 | 30 | 21 | 1 | 2.59 | 98,809 | 21.58 | 1392 |
48T15 | 48 | 30 | 20.5 | 1.5 | 2.60 | 98,898 | 21.52 | 1390 |
48T20 | 48 | 30 | 20 | 2 | 2.61 | 98,988 | 21.40 | 1388 |
48T25 | 48 | 30 | 19.5 | 2.5 | 2.59 | 990,775 | 21.55 | 1391 |
48T30 | 48 | 30 | 19 | 3 | 2.58 | 101,564 | 22.13 | 1403 |