Material | k1 and k2 (mNµm3/2) | FNmax (mN) | FNkink (mN) | hkink (µm) | Wtransition/mN (mNµm/mN) | Literature for Data Origin |
Aragonite CaCO3 (-110) | 39.396 48.962 | 1.0 | 0.4086 | 0.04644 | 0.002758 | Kearney, Phys Rev Lett 2006, 96, 255505 |
Calcite CaCO3 (100)a) | 17.911 23.176 | 10.0 | 0.3655 | 0.08266 | 0.01599 | Guillonneau, J Mater Res 2012, 22, 2551 |
Calcite CaCO3 (100)b) | 33.156 48.943 | 40.0b) | 11.869 | 0.4940 | 0.10692 | Presser, J Mater Sci 2010, 45, 2408 |
Sapphire Al2O3 | 236.05 267.08 | 90.0 | 34.326 | 0.2763 | 0.13453 | Page, J Mater Res 1992 7 450 |
Zirconium dioxide ZrO2 | 134.74 210.88 | 33.0 | 8.7514 | 0.1665 | 0.02828 | Zeng, Acta Mater 2001, 49, 3539 |
Tungsten W | 95.57 114.50 | 85.0 | 35.607 | 0.5525 | 0.070059 | Oliver-Pharr, J Mater Res 1992, 7, 1584 |
InGaAs2 (001) | 36.272 32.477 | 2.7 | 1.2703 | 0.1070 | −0.005380 | Kaupp, Scanning 2013, 35, 392 |
Mica, Muscovite KAl2[(OH,F)2/AlSi3O10)] | 34.522 3.566 | 50.0 | 11.556 | 0.4434 | 0.01016 | Hutchinson, Acta Metall Mater 40 295, 1992 |
Ce(C2O4)2(CO2H) (001) “MOF” | 52.848 64.907 | 20.0 | 8.0745 | 0.3102 | 0.06554 | Tan, J Am Chem Soc 2009, 131, 14252 |
Pine latewood radial | 0.1342 0.1705 | 1.8 | 0.5469 | 2.5625 | 0.23926 | Brandt, Acta Biomater 2000, 6, 4345 |
Pine latewood axial | 0.2098 0.3043 | 3.0 | 0.9631 | 2.7638 | 0.36510 | ditto |
Saccharin (011)c) | 1.9543 2.3179 | 6.0 | 1.7108 | 0.9426 | 0.08293 | Kira, Cryst Growth Design 2010, 10, 4650 |
Benzylidene-butyrolactone (010)c) | 0.4807 0.5724 | 2.1 | 1.0634 | 1.6671 | 0.07893 | Kaupp, Angew Chem 1996, 35, 2774 |