clay (wt%) | Clinker amount (wt%) | Compressive Strength (MPa) | Deplacement (mm) | RMF(MPa) | Young’s Modulus (MPa) |
100 | 0 | 10.37 | 1.13 | 3.20457 | 207 |
90 | 10 | 15.37 | 1.12025 | 8.2235 | 746.23 |
85 | 15 | 24.18 | 0.80956 | 10.2435 | 1237 |
80 | 20 | 30.28 | 0.62263 | 12.39684 | 1586 |
75 | 25 | 38.45 | 0.52606 | 13.41083 | 3425 |
70 | 30 | 39.18 | 0.52606 | 14.1423 | 3425 |
65 | 35 | 40.85 | 0.52606 | 16.42003 | 3484 |
60 | 40 | 42.87 | 0.52603 | 18.76814 | 3819 |
50 | 50 | 44.91 | 0.52602 | 19.43189 | 3876 |
40 | 60 | 45.91 | 0.52591 | 20.44 | 3971 |
30 | 70 | 45.53 | 0.52601 | 21.4399 | 3960 |
20 | 80 | 45.47 | 0.52606 | 21.43874 | 3954 |
10 | 90 | 45.4 | 0.52611 | 21.87758 | 3948 |
0 | 100 | 45.37 | 0.52616 | 21.74364 | 3935 |