| Modulus (GPa) | Yield Stress (MPa) | Stress at Break (MPa) | Strain at Break (%) |
LN | 2.4 ± 0.2 | 44 ± 0.0 | - | - |
LM | 1.9 ± 0.1 | 40 ± 0.0 | - | - |
HM | 2.5 ± 0.2 | 48 ± 0.0 | 43.2 ± 1.1 | 331 ± 17 |
HW | 2.2 ± 0.1 | 44 ± 0.1 | 52.7 ± 3.1 | 679 ± 15 |