Т, K | η [24] , mPa·c | η(14), mPa·c | а (15) | Т, K | η [24] , mPa·c | η(14), mPa·c | а (15) |
Тт = 887 | - | 1.755 | 3.862 | 1040 | - | 0.985 | 3.584 |
900 | - | 1.659 | 3.836 | 1060 | - | 0.925 | 3.552 |
910 | 1.59 | 1.590 | 3.816 | 1080 | 0.87 | 0.870 | 3.521 |
930 | - | 1.465 | 3.777 | 1180 | - | 0.661 | 3.377 |
950 | - | 1.354 | 3.740 | 1280 | - | 0.525 | 3.250 |
970 | - | 1.255 | 3.703 | 1380 | - | 0.431 | 3.137 |
980 | 1.21 | 1.210 | 3.685 | 1480 | - | 0.363 | 3.036 |
1000 | - | 1.127 | 3.650 | 1580 | - | 0.313 | 2.944 |
1020 | - | 1.052 | 3.617 | Tb = 1653 | - | 0.285 | 2.882 |